Mold Rubbers
Aluminum Sprue Former
Perfect contact between the mold and wax injector nozzle.
Silicone spray 400 ml.
Red Silicone Rubber in sheet of 900 g.
Vulcanizing temperature: 170 - 180 °C.
Vulcanizing time: 1 hour.
Hardness: Shore 40.
Sheet size: mm 300 x 300 x 6.
Fusimod Blue Silicone Rubber Low Shrinkage
Vulcanizing recommended temperature: 80 - 100 °C.
Vulcanizing time: 2 Minutes x mm.
Hardness: Shore 46.
Elongation (%): 610.
Tensile strenght (N/mm2): 8,9.
Tear strenght (N/mm): 17,4.
Shrinkage: minimum.
Sold in sheet of 500 g.
Sheet size: mm 330 x 180 x 6.
Fusimold Transparent Silicone Rubber Low Shrinkage
Vulcanizing recommended temperature: 80 - 100 °C.
Vulcanizing time: 2 Minutes x mm.
Hardness: Shore 46.
Elongation (%): 610.
Tensile strenght (N/mm2): 8,9.
Tear strenght (N/mm): 17,4.
Shrinkage: minimum.
Sold in sheet of 500 g.
Sheet size: mm 330 x 180 x 6.
Blue Silicone Rubber in sheet of 900 g.
Vulcanizing temperature: 170 - 180 °C.
Vulcanizing time: 1 hour.
Hardness: Shore 44 - 46.
Shrinkage: 2,5 %.
Sheet size: mm 300 x 300 x 6.
Yellow Silicone Rubber in sheet of 900 g.
Vulcanizing temperature: 170 - 180 °C.
Vulcanizing time: 1 hour.
Hardness: Shore 50.
Shrinkage: 2,5 %.
Sheet size: mm 300 x 300 x 6.
Pink Silicone Rubber in sheet of 900 g.
Vulcanizing temperature: 170 - 180 °C.
Vulcanizing time: 1 hour.
Hardness: Shore 44 - 46.
Shrinkage: 2,5 %.
Sheet size: mm 300 x 300 x 6.
Hazelnut Silicone Rubber Low Shrinkage in sheet of 900 g.
Vulcanizing temperature: 85 - 90 °C.
Vulcanizing time: 1 hour.
Hardness: Shore 44 - 46.
Shrinkage: 0,3 %.
Sheet size: mm 300 x 300 x 6.
Mustard Silicone Rubber
Mold Frames
SILAB RTV 940 Transparent silicone rubber
1 Kg. Component A + 1 Kg. Component B.
Hardness in Shore A: 42±2
SILAB RTV 940 is a bi-component addition cured RTV silicone rubber (base and catalyst with ratio 1:1) which vulcanizes at room temperature.
SILAB RTV 940 is compatible with all plasters, coatings, polyurethane resins and acrylic resins.
Fusimod Blue Silicone Rubber - 5 Kg.