Squared ceramic crucible cm 6x6
Squared ceramic crucible cm 6x6
Squared ceramic crucible cm 6x6
Graphite Crucible for 2 kg Melting Furnace
Yellow Alloy for gold A182N ultracast
Cast iron ingot mold mm 90 x 35 x 35
Ingot Size: mm 90 x 35 x 35.
Gold capacity: g. 1700.
Made in Italy.
Freeman Flakes Injection Wax - Filigree Pink
Pack of 454 g.
Injection Temperature: 73º C / 165º F.
Very high detail.
Ingot Mold for wire
Replacement gasket for manual pump for wax injectors
External diameter 30 mm.
Internal diameter 17 mm.
Rubber Mixing Bowl Ø 160 mm
Height 140 mm.
Highly-flexible vulcanized rubber bowl.
Top quality.
Zinc in drops
Sale by weight.
Unit of measure: Grams.
Blue Silicone Rubber in sheet of 900 g.
Vulcanizing temperature: 170 - 180 °C.
Vulcanizing time: 1 hour.
Hardness: Shore 44 - 46.
Shrinkage: 2,5 %.
Sheet size: mm 300 x 300 x 6.
Graphite Crucible for 1 kg Melting Furnace
Graphite Crucible for Induction Melting Machines CEIA F1
Replacement manual pump for wax injectors
1/4" male thread.
Made in Italy.
Fusimod Blue Silicone Rubber Low Shrinkage
Vulcanizing recommended temperature: 80 - 100 °C.
Vulcanizing time: 2 Minutes x mm.
Hardness: Shore 46.
Elongation (%): 610.
Tensile strenght (N/mm2): 8,9.
Tear strenght (N/mm): 17,4.
Shrinkage: minimum.
Sold in sheet of 500 g.
Sheet size: mm 330 x 180 x 6.
Vulcanizer
Model gypsum
Yellow Silicone Rubber in sheet of 900 g.
Vulcanizing temperature: 170 - 180 °C.
Vulcanizing time: 1 hour.
Hardness: Shore 50.
Shrinkage: 2,5 %.
Sheet size: mm 300 x 300 x 6.
Brass in drops
Colour: yellow.
This alloy can be used only for lost-wax casting.
To purchase please select desired package.
Fusimod Blue Silicone Rubber - 5 Kg.
Cast iron ingot mold g. 5900
O-rings and gaskets replacement kit for Wax Injector 1,5 Kg.
To replace worn-out o-rings and gaskets of Wax Injector.
Includes: No. 5 o-rings. + No. 1 Gasket for pump.
Soldering alloy for White gold 18 Kt
To purchase please select desired hardness.
Carat: 18 kt.
Color: White.
INDICATIONS FOR SUGGESTED USE
Melting temperature: 970° C.
Bracket temperature: 70° C.
Bracket casting cooling: immediate in lukewarm water (about 40° C).
Annealing: 520° C for 20 minutes followed by rapid cooling in hot water (min. 40 ° C).
Flow temperature: 670° C.
IMPORTANT: the brackets to be used must be vertical and closed on both sides. Open ingot molds cannot be used because the plates thus obtained break upon rolling.
Granular Borax Powder
Bottle of 1 kg.
R&R ULTRA-VEST investment
SILAB RTV 940 Transparent silicone rubber
1 Kg. Component A + 1 Kg. Component B.
Hardness in Shore A: 42±2
SILAB RTV 940 is a bi-component addition cured RTV silicone rubber (base and catalyst with ratio 1:1) which vulcanizes at room temperature.
SILAB RTV 940 is compatible with all plasters, coatings, polyurethane resins and acrylic resins.
White Alloy for gold OB307W1 Legor
Universal for 9 kt and 14 kt.
Support for mounting wax trees
Available in two lengths, 200 and 250 mm.
Made in Italy.
To purchase please select the desired size.
Graphite Crucible for 3 kg Melting Furnace
Cast iron ingot mold mm 70 x 35 x 25
Ingot Size: mm 70 x 35 x 25.
Gold capacity: g. 950.
Made in Italy.
Freeman Flakes Injection Wax - Turquoise
Injection Temperature: 71º C / 160º F.
Pack of 454 g.
All-purpose injection wax.
Freeman Flakes Injection Wax - Carvable Purple
Pack of 454 g.
Injection Temperature: 76-79ºC / 170-175ºF.
Superior carvability.
Ceramic Stirring Rod
Lenght 250 mm.
Grey Ceramic Stirring Rod
Lenght 300 mm.
Soldering alloy for yellow gold 18 Kt.
Carat: 18 kt.
Color: Yellow.
INDICATIONS FOR SUGGESTED USE
Melting temperature: 960° C.
Bracket temperature: 70° C.
Bracket casting cooling: immediate in lukewarm water (about 40° C).
Annealing: 520° C for 20 minutes followed by rapid cooling in hot water (min. 40 ° C).
Flow temperature: 650° C.
IMPORTANT: the brackets to be used must be vertical and closed on both sides. Open ingot molds cannot be used because the plates thus obtained break upon rolling.
Squared ceramic crucible cm 10x10
Red Silicone Rubber in sheet of 900 g.
Vulcanizing temperature: 170 - 180 °C.
Vulcanizing time: 1 hour.
Hardness: Shore 40.
Sheet size: mm 300 x 300 x 6.