Yellow Alloy for gold A182N ultracast
Yellow Alloy for gold A182N ultracast
Yellow Alloy for gold A182N ultracast
Composition: Copper 90% - Tin 10%.
Fusimod Blue Silicone Rubber Low Shrinkage
Vulcanizing recommended temperature: 80 - 100 °C.
Vulcanizing time: 2 Minutes x mm.
Hardness: Shore 46.
Elongation (%): 610.
Tensile strenght (N/mm2): 8,9.
Tear strenght (N/mm): 17,4.
Shrinkage: minimum.
Sold in sheet of 500 g.
Sheet size: mm 330 x 180 x 6.
O-rings and gaskets replacement kit for Wax Injector 1,5 Kg.
To replace worn-out o-rings and gaskets of Wax Injector.
Includes: No. 5 o-rings. + No. 1 Gasket for pump.
Mustard Silicone Rubber
Nickel Safe white Alloy Pandora ROLLY
High performance standard alloy for 18 carats, for mechanical works.
Color: white - standard color coordinates: L * = 85.5 a * = 2.8 b * = 14.5.
Nickel release UNI EN 1811: 2011: 0.14 μg / cm2 / week.
Fusimod Blue Silicone Rubber - 5 Kg.
Laboratory Vibrator
Boric acid powder for fusion
Bottle 1 kg.
Support for mounting wax trees
Available in two lengths, 200 and 250 mm.
Made in Italy.
To purchase please select the desired size.
Ceramic Stirring Rod
Lenght 250 mm.
Squared ceramic crucible cm 7x7
R&R AURUM investment
Ingot Mold for wire
Replacement gasket for manual pump for wax injectors
External diameter 30 mm.
Internal diameter 17 mm.
Yellow Alloy for gold 2P18 Pandora
Cast iron ingot mold mm 90 x 35 x 35
Ingot Size: mm 90 x 35 x 35.
Gold capacity: g. 1700.
Made in Italy.
Graphite Crucible for Induction Melting Machines CEIA F1
White Alloy EM
Composition: Copper 88% - Tin 12%.
Freeman Flakes Injection Wax - Flexible Blue
Injection Temperature: 76º C / 170º F.
Pack of 454 g.
Highest Flexibility.
Surgical Scalpel Blade No.10
Soldering alloy for yellow gold 18 Kt.
Carat: 18 kt.
Color: Yellow.
INDICATIONS FOR SUGGESTED USE
Melting temperature: 960° C.
Bracket temperature: 70° C.
Bracket casting cooling: immediate in lukewarm water (about 40° C).
Annealing: 520° C for 20 minutes followed by rapid cooling in hot water (min. 40 ° C).
Flow temperature: 650° C.
IMPORTANT: the brackets to be used must be vertical and closed on both sides. Open ingot molds cannot be used because the plates thus obtained break upon rolling.
Stainless steel Casting Flasks
Use with Tree Sprue base.
To purchase please select desided size.
Mold Frames
Wax Injector - 1.5 kg.
Equipped with pressure gauge and hand-operated pump.
Three different interchangeable nozzles supplied.
Wax capacity: 1,5 kg.
Max temperature: 85° C.
Made in Italy.
Freeman Flakes Injection Wax - Tuf Guy Green
Pack of 454 g.
Injection Temperature: 76ºC / 170ºF.
High toughness.
Aluminum Sprue Former
Perfect contact between the mold and wax injector nozzle.
Wax Injector 145°C - 1.5 kg
See-Thru Mold Frame
Contains 2 glass cover plates with 2 metal clamps and one center frame with a sprue former for making the sprue for the model.
Size: mm 53 x 50 x 90 h.
Made in USA.
Replacement manual pump for wax injectors
1/4" male thread.
Made in Italy.
Wax Injector
Capacity 1,5 kg.
Max temperature: 85° C.
Power: 160 Watt.
Size: mm 160 x 160 x 520 h.
Made in Italy.
Graphite Crucible for gas Furnace
Cuttlefish bones for casting
Box 1 kg.
Graphite Crucible for 0,5 kg Melting Furnace
SILAB RTV 940 Transparent silicone rubber
1 Kg. Component A + 1 Kg. Component B.
Hardness in Shore A: 42±2
SILAB RTV 940 is a bi-component addition cured RTV silicone rubber (base and catalyst with ratio 1:1) which vulcanizes at room temperature.
SILAB RTV 940 is compatible with all plasters, coatings, polyurethane resins and acrylic resins.