Rubber Mixing Bowl Ø 160 mm
Rubber Mixing Bowl Ø 160 mm
Height 140 mm.
Highly-flexible vulcanized rubber bowl.
Top quality.
Rubber Mixing Bowl Ø 160 mm
Height 140 mm.
Highly-flexible vulcanized rubber bowl.
Top quality.
Pink Silicone Rubber in sheet of 900 g.
Vulcanizing temperature: 170 - 180 °C.
Vulcanizing time: 1 hour.
Hardness: Shore 44 - 46.
Shrinkage: 2,5 %.
Sheet size: mm 300 x 300 x 6.
Graphite Crucible for 0,5 kg Melting Furnace
Mold Frames
Ingot Mold for wire
Tongs for crucibles
Graphite Stirring Rod 300 mm
Casting Vacuum Machine
Squared ceramic crucible cm 10x10
Yellow Alloy for gold A182N ultracast
Aluminum Sprue Former
Perfect contact between the mold and wax injector nozzle.
Delftclay standard kit 2 kg.
Includes:
- 2 Kg. of sand;
- Set of Aluminium rings Ø mm 60;
- Users Manual.
Surgical Scalpel Blade No.12
Fusimod Blue Silicone Rubber - 5 Kg.
Wax injection valve for Wax Injector complete with nozzle
Spare part for manual wax injector.
Made in Italy.
Freeman Flakes Injection Wax - Filigree Pink
Pack of 454 g.
Injection Temperature: 73º C / 165º F.
Very high detail.
R&R AURUM investment
Ceramic Stirring Rod
Lenght 300 mm.
Yellow Silicone Rubber in sheet of 900 g.
Vulcanizing temperature: 170 - 180 °C.
Vulcanizing time: 1 hour.
Hardness: Shore 50.
Shrinkage: 2,5 %.
Sheet size: mm 300 x 300 x 6.
Soldering alloy for White gold 18 Kt
To purchase please select desired hardness.
Carat: 18 kt.
Color: White.
INDICATIONS FOR SUGGESTED USE
Melting temperature: 970° C.
Bracket temperature: 70° C.
Bracket casting cooling: immediate in lukewarm water (about 40° C).
Annealing: 520° C for 20 minutes followed by rapid cooling in hot water (min. 40 ° C).
Flow temperature: 670° C.
IMPORTANT: the brackets to be used must be vertical and closed on both sides. Open ingot molds cannot be used because the plates thus obtained break upon rolling.
Squared ceramic crucible cm 6x6
Vulcanizer
Freeman Flakes Injection Wax - Tuf Guy Green
Pack of 454 g.
Injection Temperature: 76ºC / 170ºF.
High toughness.
Soldering alloy for yellow gold 18 Kt.
Carat: 18 kt.
Color: Yellow.
INDICATIONS FOR SUGGESTED USE
Melting temperature: 960° C.
Bracket temperature: 70° C.
Bracket casting cooling: immediate in lukewarm water (about 40° C).
Annealing: 520° C for 20 minutes followed by rapid cooling in hot water (min. 40 ° C).
Flow temperature: 650° C.
IMPORTANT: the brackets to be used must be vertical and closed on both sides. Open ingot molds cannot be used because the plates thus obtained break upon rolling.
Freeman Flakes Injection Wax - Aqua Green
Injection Temperature: 71º C / 160º F.
Pack of 454 g.
All-purpose injection wax.
Cast iron ingot mold g. 2600
Laboratory Vibrator