Graphite Crucible for 3 kg Automatic Melting Furnace
Graphite Crucible for 3 kg Melting Furnace
Graphite Crucible for 3 kg Melting Furnace
R&R ULTRA-VEST investment
Surgical Handles No.3
Graphite Crucible for Induction Melting Machines CEIA F1
See-Thru Mold Frame
Contains 2 glass cover plates with 2 metal clamps and one center frame with a sprue former for making the sprue for the model.
Size: mm 53 x 50 x 90 h.
Made in USA.
R&R ULTRA-VEST investment
Zinc in drops
Sale by weight.
Unit of measure: Grams.
Squared ceramic crucible cm 7x7
Grey Ceramic Stirring Rod
Lenght 300 mm.
Mold Frames
Freeman Flakes Injection Wax - Turquoise
Injection Temperature: 71º C / 160º F.
Pack of 454 g.
All-purpose injection wax.
Adjustable Ingot Mold
Mold can be made smaller by adjusting the sides.
Heavy, precisely machined and built to last a lifetime.
Made in Italy.
To purchase please select desired size.
Fusimold Transparent Silicone Rubber Low Shrinkage
Vulcanizing recommended temperature: 80 - 100 °C.
Vulcanizing time: 2 Minutes x mm.
Hardness: Shore 46.
Elongation (%): 610.
Tensile strenght (N/mm2): 8,9.
Tear strenght (N/mm): 17,4.
Shrinkage: minimum.
Sold in sheet of 500 g.
Sheet size: mm 330 x 180 x 6.
Mold Frames
R&R PLASTICAST investment
Cast iron ingot mold g. 2600
Brass in drops
Colour: yellow.
This alloy can be used only for lost-wax casting.
To purchase please select desired package.
Granular Borax Powder
Bottle of 1 kg.
Soldering alloy for yellow gold 18 Kt.
Carat: 18 kt.
Color: Yellow.
INDICATIONS FOR SUGGESTED USE
Melting temperature: 960° C.
Bracket temperature: 70° C.
Bracket casting cooling: immediate in lukewarm water (about 40° C).
Annealing: 520° C for 20 minutes followed by rapid cooling in hot water (min. 40 ° C).
Flow temperature: 650° C.
IMPORTANT: the brackets to be used must be vertical and closed on both sides. Open ingot molds cannot be used because the plates thus obtained break upon rolling.
Graphite Crucible for gas Furnace
Wax Injector - 1.5 kg.
Equipped with pressure gauge and hand-operated pump.
Three different interchangeable nozzles supplied.
Wax capacity: 1,5 kg.
Max temperature: 85° C.
Made in Italy.
Soldering alloy for White gold 18 Kt
To purchase please select desired hardness.
Carat: 18 kt.
Color: White.
INDICATIONS FOR SUGGESTED USE
Melting temperature: 970° C.
Bracket temperature: 70° C.
Bracket casting cooling: immediate in lukewarm water (about 40° C).
Annealing: 520° C for 20 minutes followed by rapid cooling in hot water (min. 40 ° C).
Flow temperature: 670° C.
IMPORTANT: the brackets to be used must be vertical and closed on both sides. Open ingot molds cannot be used because the plates thus obtained break upon rolling.
Fusimod Blue Silicone Rubber Low Shrinkage
Vulcanizing recommended temperature: 80 - 100 °C.
Vulcanizing time: 2 Minutes x mm.
Hardness: Shore 46.
Elongation (%): 610.
Tensile strenght (N/mm2): 8,9.
Tear strenght (N/mm): 17,4.
Shrinkage: minimum.
Sold in sheet of 500 g.
Sheet size: mm 330 x 180 x 6.
Squared ceramic crucible cm 5x5
Red Silicone Rubber in sheet of 900 g.
Vulcanizing temperature: 170 - 180 °C.
Vulcanizing time: 1 hour.
Hardness: Shore 40.
Sheet size: mm 300 x 300 x 6.
Ingot Mold for wire
Fusimod Blue Silicone Rubber - 5 Kg.