Red Alloy for gold 5P18/L Pandora
Soldering alloy for yellow gold 18 Kt.
Carat: 18 kt.
Color: Yellow.
INDICATIONS FOR SUGGESTED USE
Melting temperature: 960° C.
Bracket temperature: 70° C.
Bracket casting cooling: immediate in lukewarm water (about 40° C).
Annealing: 520° C for 20 minutes followed by rapid cooling in hot water (min. 40 ° C).
Flow temperature: 650° C.
IMPORTANT: the brackets to be used must be vertical and closed on both sides. Open ingot molds cannot be used because the plates thus obtained break upon rolling.
Copper 99.99 in drops
Made in Italy.
To purchase please select desired package.
Casting Vacuum Machine
Cast iron ingot mold g. 5900
Squared ceramic crucible cm 10x10
Nickel Safe white Alloy Pandora ROLLY
High performance standard alloy for 18 carats, for mechanical works.
Color: white - standard color coordinates: L * = 85.5 a * = 2.8 b * = 14.5.
Nickel release UNI EN 1811: 2011: 0.14 μg / cm2 / week.
Graphite Crucible for Induction Melting Machines CEIA F1
Wax Injector - 1.5 kg.
Equipped with pressure gauge and hand-operated pump.
Three different interchangeable nozzles supplied.
Wax capacity: 1,5 kg.
Max temperature: 85° C.
Made in Italy.
Fusimod Blue Silicone Rubber Low Shrinkage
Vulcanizing recommended temperature: 80 - 100 °C.
Vulcanizing time: 2 Minutes x mm.
Hardness: Shore 46.
Elongation (%): 610.
Tensile strenght (N/mm2): 8,9.
Tear strenght (N/mm): 17,4.
Shrinkage: minimum.
Sold in sheet of 500 g.
Sheet size: mm 330 x 180 x 6.
Freeman Flakes Injection Wax - Aqua Green
Injection Temperature: 71º C / 160º F.
Pack of 454 g.
All-purpose injection wax.
Replacement gasket for manual pump for wax injectors
External diameter 30 mm.
Internal diameter 17 mm.
Cast iron ingot mold mm 70 x 35 x 25
Ingot Size: mm 70 x 35 x 25.
Gold capacity: g. 950.
Made in Italy.
Granular Borax Powder
Bottle of 1 kg.
Grey Ceramic Stirring Rod
Lenght 300 mm.
Squared ceramic crucible cm 5x5
Graphite Crucible for 1 kg Melting Furnace
Wax injection valve for Wax Injector complete with nozzle
Spare part for manual wax injector.
Made in Italy.
Freeman Flakes Injection Wax - Carvable Purple
Pack of 454 g.
Injection Temperature: 76-79ºC / 170-175ºF.
Superior carvability.
Yellow Alloy for gold 2P18 Pandora
Freeman Flakes Injection Wax - Turquoise
Injection Temperature: 71º C / 160º F.
Pack of 454 g.
All-purpose injection wax.
Yellow Silicone Rubber in sheet of 900 g.
Vulcanizing temperature: 170 - 180 °C.
Vulcanizing time: 1 hour.
Hardness: Shore 50.
Shrinkage: 2,5 %.
Sheet size: mm 300 x 300 x 6.
Mixing Spatula
Replacement manual pump for wax injectors
1/4" male thread.
Made in Italy.
Tongs for crucibles
Cast iron ingot mold mm 90 x 35 x 35
Ingot Size: mm 90 x 35 x 35.
Gold capacity: g. 1700.
Made in Italy.
Support for mounting wax trees
Available in two lengths, 200 and 250 mm.
Made in Italy.
To purchase please select the desired size.
Delftclay standard kit 2 kg.
Includes:
- 2 Kg. of sand;
- Set of Aluminium rings Ø mm 60;
- Users Manual.
Graphite Crucible for 3 kg Melting Furnace
Laboratory Vibrator
Copper in sticks
Kevlar gloves
Soldering alloy for White gold 18 Kt
To purchase please select desired hardness.
Carat: 18 kt.
Color: White.
INDICATIONS FOR SUGGESTED USE
Melting temperature: 970° C.
Bracket temperature: 70° C.
Bracket casting cooling: immediate in lukewarm water (about 40° C).
Annealing: 520° C for 20 minutes followed by rapid cooling in hot water (min. 40 ° C).
Flow temperature: 670° C.
IMPORTANT: the brackets to be used must be vertical and closed on both sides. Open ingot molds cannot be used because the plates thus obtained break upon rolling.