Zinc in drops
Zinc in drops
Sale by weight.
Unit of measure: Grams.
Alloys
Zinc in drops
Sale by weight.
Unit of measure: Grams.
Composition: Copper 88% - Tin 12%.
Yellow Alloy for gold 2P18 Pandora
White Alloy for gold ELA2 Pandora
Nickel release UNI EN 1811: 2011: 0.05 μg / cm2 / week - COMPLIANT (max. 0.88 μg / cm2 / week).
Nickel Safe Alloy, universal for 14 kt and 18 kt.
This alloy can be used for lost-wax casting and for mechanical working processes in general.
White Alloy for gold OB307W1 Legor
Universal for 9 kt and 14 kt.
Copper 99.99 in drops
Made in Italy.
To purchase please select desired package.
White Alloy EM
Brass in drops
Colour: yellow.
This alloy can be used only for lost-wax casting.
To purchase please select desired package.
Red Alloy for gold 5P18/L Pandora
Composition: Copper 90% - Tin 10%.
Yellow Alloy for gold A182N ultracast
Nickel Safe white Alloy Pandora ROLLY
High performance standard alloy for 18 carats, for mechanical works.
Color: white - standard color coordinates: L * = 85.5 a * = 2.8 b * = 14.5.
Nickel release UNI EN 1811: 2011: 0.14 μg / cm2 / week.
Copper in sticks
Soldering alloy for White gold 18 Kt
To purchase please select desired hardness.
Carat: 18 kt.
Color: White.
INDICATIONS FOR SUGGESTED USE
Melting temperature: 970° C.
Bracket temperature: 70° C.
Bracket casting cooling: immediate in lukewarm water (about 40° C).
Annealing: 520° C for 20 minutes followed by rapid cooling in hot water (min. 40 ° C).
Flow temperature: 670° C.
IMPORTANT: the brackets to be used must be vertical and closed on both sides. Open ingot molds cannot be used because the plates thus obtained break upon rolling.
Soldering alloy for yellow gold 18 Kt.
Carat: 18 kt.
Color: Yellow.
INDICATIONS FOR SUGGESTED USE
Melting temperature: 960° C.
Bracket temperature: 70° C.
Bracket casting cooling: immediate in lukewarm water (about 40° C).
Annealing: 520° C for 20 minutes followed by rapid cooling in hot water (min. 40 ° C).
Flow temperature: 650° C.
IMPORTANT: the brackets to be used must be vertical and closed on both sides. Open ingot molds cannot be used because the plates thus obtained break upon rolling.